LDPE/Low Density Polyethylene Plastic Raw Granular

Product Name: LDPE/Low Density Polyethylene Plastic Raw Granular Model NO.: LDPE Material: Low Density Polyethylene/LDPE Usage: General Plastics, Engineering Plastics, Specialty Plastics Plastic Properties After Heated: Thermoplastic Plastics Plastic Forming Method: Lamination Color: White Place of Origin: Hebei China (Mainland) CAS: 9002-88-4 Hs: 39012000 Brand Name: Sinopec Service: OEM/ODM Trademark: OEM/ODM Transport Package: 25kg/50kg Per Plastic Bag Specification: SGS CE Origin: China Mainland HS Code: 39012000 Product Description Specification:

film grade

Item	Test condition	Test Method	Value	Unit
Density		ISO 1183	0.944-0.955	g/cm3
MFR	190°C/2.16kg	ISO 1133	0.03-0.07	g/10min
Tensile strength at yield		ISO 527-2	22	MPa
Elongation at break		ISO 527-2	>350	%
ESCR	F50,50°C,100%	ASTM D-1693A	1000	h
VICAT		ASTM D-1525	126	°C

blow grade

Item	Test Condition	Test Method	Value	Unit
Density		ISO 1183	0.950~0.955	g/cm
MFR	190°C/2.16kg	ISO 1133	1.7~2.5	g/10min
Tensile strength at yield		ISO 527-2	24	MPa
Elongation at break		ISO 527-2	>600	%

injection grade

Item	Test Condition	Test Method	Value	Unit
MFR	190°C/2.16kg	ASTM D-1238	20	g/10min
Density	---	ASTM D-792	0.954	g/cm3
Tensile strength at yiled	---	ASTM D-638	28	MPa
Elongation at break	---	ASTM D-638	250	%
Impact tensile strength	---	ASTM D-1822	42	kJ/m2
ESCR		ASTM D-1693	3	---
VACIT	---	ASTM D-1525	127	°C

LDPE Injection Grade
Tests Value Unit
Melt Flow Rate (MFR) 15 g/10min
Density 0.922 g/cm3
Tensile Yield Strength 7 Mpa
Elongation at Break 75 %
Wien Softening Point 85 ° C
Packing
In 25 kg PP woven bags, 20MT/20'FCL

LDPE film grade

Tests Value Unit
Melt Flow Rate (MFR) 2 g/10min Density 0.9225 g/cm3
Tensile Strength 9 Mpa
Elongation at Break 500 %
Fish eye max(0.3-2mm) 30 n/1200cm2
Stripes 20 cm/20m3
Packing
In 25 kg PP woven bags, 20MT/20'FCL